Calcium silicate hydrate
Calcium silicate hydrate (or C-S-H) is the main product of the hydration of Portland cement and is primarily responsible for the strength in cement based materials (e.g. concrete).
Preparation
Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water. This reaction typically is expressed as:
The stoichiometry of C-S-H in cement paste is variable and the state of chemically and physically bound water in its structure is not transparent, which is why "-" is used between C, S, and H.[1]
Synthetic C-S-H can be prepared from the reaction of CaO and SiO2 in water or through the double precipitation method using various salts. These methods provide the flexibility of producing C-S-H at specific C/S (Ca/Si, or CaO/SiO2) ratios. The C-S-H from cement phases can also be treated with an ammonium nitrate solution in order to induce calcium leaching, and so to achieve a given C/S ratio.
Properties
C-S-H is a nano sized material[2][3] with some degree of crystallinity as observed by X-ray diffraction techniques.[4] The underlying atomic structure of C-S-H is similar to the naturally occurring mineral tobermorite.[5] It has a layered geometry with calcium silicate sheet structure separated by an interlayer space. The silicates in C-S-H exist as dimers, pentamers and 3n-1 chain units [6][7] (where n is an integer greater than 0) and calcium ions are found to connect these chains making the three dimensional nano structure as observed by dynamic nuclear polarisation surface-enhanced nuclear magnetic resonance.[8] The exact nature of the interlayer remains unknown. One of the greatest difficulties in characterising C-S-H is due to its variable stoichiometry.
The scanning electron microscope micrographs of C-S-H does not show any specific crystalline form. They usually manifest as foils or needle/oriented foils.
Synthetic C-S-H can be divided in two categories separated at the Ca/Si ratio of about 1.1. There are several indications that the chemical, physical and mechanical characteristics of C-S-H varies noticeably between these two categories.[9][10]
See also
Other C-S-H minerals:
- Afwillite – Nesosilicate alteration mineral also sometimes found in hydrated cement paste
- Gyrolite – Rare phyllosilicate mineral crystallizing in spherules (a rare mineral from hydrothermal alteration, or an ageing product of alkali-silica reaction)
- Jennite – Inosilicate alteration mineral in metamorphosed limestone and in skarn
- Thaumasite – Complex calcium silicate hydrate mineral
- Tobermorite – Inosilicate alteration mineral in metamorphosed limestone and in skarn
Other calcium aluminium silicate hydrate, (C-A-S-H) minerals:
- Hydrogarnet
- Hydrotalcite – Hydrated Mg-Al layered double hydroxide (LDH) containing carbonate anions
Mechanisms of formation of C-S-H phases:
- Alkali–silica reaction – Chemical reaction that damages concrete
- Alkali–aggregate reaction – Expansive chemical reaction damaging concrete
- Energetically modified cement – Class of cements, mechanically processed to transform reactivity
- Pozzolanic reaction
References
- ^ "Portland Cement Hydration" (PDF). Archived from the original (PDF) on 2017-02-15. Retrieved 2013-02-21.
- ^ Allen, Andrew J.; Thomas, Jeffrey J.; Jennings, Hamlin M. (25 March 2007). "Composition and density of nanoscale calcium–silicate–hydrate in cement". Nature Materials. 6 (4): 311–316. Bibcode:2007NatMa...6..311A. doi:10.1038/nmat1871. PMID 17384634.
- ^ Andalibi, M. Reza; Kumar, Abhishek; Srinivasan, Bhuvanesh; Bowen, Paul; Scrivener, Karen; Ludwig, Christian; Testino, Andrea (2018). "On the mesoscale mechanism of synthetic calcium–silicate–hydrate precipitation: a population balance modeling approach". Journal of Materials Chemistry A. 6 (2): 363–373. doi:10.1039/C7TA08784E. ISSN 2050-7488. S2CID 103781671.
- ^ Renaudin, Guillaume; Russias, Julie; Leroux, Fabrice; Frizon, Fabien; Cau-dit-Coumes, Céline (December 2009). "Structural characterization of C–S–H and C–A–S–H samples—Part I: Long-range order investigated by Rietveld analyses". Journal of Solid State Chemistry. 182 (12): 3312–3319. Bibcode:2009JSSCh.182.3312R. doi:10.1016/j.jssc.2009.09.026.
- ^ Taylor, Harry F.W. (June 1986). "Proposed Structure for Calcium Silicate Hydrate Gel". Journal of the American Ceramic Society. 69 (6): 464–467. doi:10.1111/j.1151-2916.1986.tb07446.x.
- ^ Cong, Xiandong; Kirkpatrick, R.James (April 1996). "29Si and 17O NMR investigation of the structure of some crystalline calcium silicate hydrates". Advanced Cement Based Materials. 3 (3–4): 133–143. doi:10.1016/S1065-7355(96)90045-0.
- ^ Brunet, F.; Bertani, Ph.; Charpentier, Th.; Nonat, A.; Virlet, J. (October 2004). "Application of Si Homonuclear and H− Si Heteronuclear NMR Correlation to Structural Studies of Calcium Silicate Hydrates". The Journal of Physical Chemistry B. 108 (40): 15494–15502. doi:10.1021/jp031174g.
- ^ Kumar, Abhishek; Walder, Brennan J.; Kunhi Mohamed, Aslam; Hofstetter, Albert; Srinivasan, Bhuvanesh; Rossini, Aaron J.; Scrivener, Karen; Emsley, Lyndon; Bowen, Paul (7 July 2017). "The Atomic-Level Structure of Cementitious Calcium Silicate Hydrate". The Journal of Physical Chemistry C. 121 (32): 17188–17196. doi:10.1021/acs.jpcc.7b02439.
- ^ "Archived copy". Archived from the original on 2015-03-15. Retrieved 2013-06-01.
{{cite web}}
: CS1 maint: archived copy as title (link) - ^ "Potential Application of Nanotechnology on Cement Based Materials" (PDF). Archived from the original (PDF) on 2012-02-17. Retrieved 2013-02-21.